Product Description The product is designed for the level of the company bearing refractory grade steel components and fire protection design and production of thick-coated flame-retardant coating. The paint sprayed on the surface of the steel components, relying on their own when a fire is not flammable coating and low thermal conductivity to form a protective layer of fire-resistant insulation, fire retardation direct invasion of the load-bearing components, thereby effectively improving the fire resistance of steel structures . Since the product has not corrode steel, not from a chemical reaction with any anti-corrosion primer, odorless, light weight coated (also relatively light weight structural loads), large area coating unit does not produce smoke when a fire, does not release harmful gases and other characteristics, it is applied to a variety of new construction, expansion and renovation of industrial and civil engineering steel load-bearing fire painting and fire protection components. After the construction of the wall can be brushed on the surface of decorative paint better. Technical standards in line with the national standard GB 14907-2002 technical indicators. Before construction process fireproof paint coating, rust and rust primer coating steel member surface shall meet the design requirements and the existing national specification should completely remove dust on the surface of steel components, grease and other debris. Construction of fire retardant paint coating should be done before the next and the interior will not be damaged by the follow-up project conditions. Construction, does not require fire protection for walls, doors, windows, and other components, such as machinery and equipment should be shielded to protect. Before painting, powder added to the amount of water required to stir, so that was no lumps of viscous fluid state. Thin consistency should facilitate the construction, not flowing, firmly bonded appropriate. For wide large steel components, should be retrofitted with steel mesh to prevent the paint off or separation. Construction, using bump bucket gun, the air pressure is 0.6 ~ 0.8MPa, gun hole diameter is preferably 6 ~ 10mm, the gun perpendicular to the surface coating component to 40 ~ 60cm appropriate. Construction of the first pass when spraying should not be too thick, until the basic drying or curing, then spray down times. From the second pass, each pass coating thickness can be thickened under the circumstances, to not flowing as the standard, until it reaches the required thickness can be. Reference amount 0.75kg / m / mm. Precautions during construction and coating drying and curing, the ambient temperature should be maintained at 5 ~ 38 ℃, relative humidity not more than 80%, the air should circulate. After the completion of the construction of the product subject to a 60-day maintenance period. When the component surface condensation, not construction. Construction process, we should pay attention to the coating thickness measurements according to fire resistance. The product is water-based fire retardant paint, coatings and therefore either during construction or after completion of construction shall be in the room or shelter shed to avoid the rain. Do not wet the powder; preparation of a good paint must be used within 30 minutes. Packaging and storage Packing: 25kg / bag. Storage: ventilated, dry coffers, separated from fire, away from heat body to prevent freezing or exposure. Shelf life is one year.